Why should cathodic protection and a coating be used together to protect against corrosion?
No coating is flawless, so cathodic protection is an effective complementary method to protect structures in a corrosive environment.
Applying aprotective coatingto metallic surfaces is the most effective method to mitigate corrosion damage. According to aNational Association of Corrosion Engineers (NACE)report, more than$100 billion dollars is spent in the U.S.to control corrosion by the application of eitherorganicormetallic coatings. Fifty percent of the corrosion damage cost is preventable with 85 percent of that related to coatings. Thus, coatings play an important role in protecting metallic materials against corrosion.
The Impact of Coating Defects
However, coatings are not perfect. In reality, no coating is entirely free of defects even when freshly applied. The presence of defects is considered inevitable. Some of these defects appear during coating production and some of them stem from handling and improper application. (Learn more about these in the article5 Coating Defects That Can Be Avoided By Adhering To Coating Specs.) Also, some other defects form during the coating's service lifetime, which is called “coating degradation.” This degradation can be caused by mechanical stress (e.g., soil expansion and contraction during wet and dry conditions), chemical reactions (presence of aggressive ions such aschloride ions),UV exposure, bacterial attack (such as anaerobicsulfate-reducing bacteria (SRB)或阴极disbondingdue to over-cathodic protection.
Table 1 shows how coatings fail with time. Coatings always have some small defects when they are applied. The density of defects will increase over time.
Table 1.Guide to coating breakdown for offshore structures.
Initial |
Mean |
Final |
|
---|---|---|---|
Lifetime (years) |
Coating breakdown (%) |
||
10 |
2 |
7 |
20 |
20 |
2 |
15 |
30 |
30 |
2 |
25 |
60 |
40 |
2 |
40 |
90 |
Source:L.L. Sheir, R.A. Jarman, and G.T. Burstein; “Corrosion”, Volume 2: “Corrosion Control”, 3rd edition, Butterworth Heinemann, ISBN 0-7506-1077-8, PP 10.3 – 10.28
Here, the question is whether we can produce a coating with zero defects. The answer is no in practical application but we might have a defect-free coating in theory. Producing a defect-free coating is impossible or at least not feasible on a mass production scale. Figure 1 shows how the cost of coating increases when we try to reduce the defect density.
Free Download:How To Detect Pipe Corrosion in Underground Force Mains, Plus Must-Have Corrosion Detection Equipment |
Figure 1.Illustrates the relationship between the cost to protect a structure by cathodic protection (brown line), protective coatings (blue line), or combined methods (black line) for various coverage areas. There is an overall benefit when a good coating application is combined with cathodic protection (optimized situation).
Source:L.L. Sheir, R.A. Jarman, and G.T. Burstein; “Corrosion”, Volume 2: “Corrosion Control”, 3rd edition, Butterworth Heinemann, ISBN 0-7506-1077-8.
很明显,高效的有限公司atings cost more. When thecoverageof coating is less than approximately 80 percent there is a linear relationship between cost and percent of coverage. However, if a high degree of coverage is demanded, this becomes a logarithmic relationship. It means that the cost required to increase the efficiency of the coatings from 98 to 99 percent (one percent) can be 10 times more than when we increase the efficiency of coatings from 65 to 66 percent (again one percent). Higher cost is a result of thicker coatings, the use high-tech inspection techniques and repairing individual defects. Therefore, it is not possible to eliminate all defects in reality.
Adding Supplementary Cathodic Protection
Sometimes it is advantageous to use another protection method to supplement coatings, which is why we use cathodic protection. (Learn aboutThe Basics of Cathodic Protection.)
Let’s see the issue from a different perspective. Can we protect a bare structure with only cathodic protection?
Theoretically it is possible. However, cathodic protection of a bare structureis usually not cost effective. Even in a near neutral pH environment a considerable electric current is required to protect a structure. Table 2 shows the requiredcurrent densitiesto protect a steel pipeline buried in various soil types. As shown, the required current density to protect a steel pipeline will be reduced more than five hundredfold when a protective coating is applied.
Table 2.Required current densities to protect buried steel structures in different conditions.
Structure type |
Type of soil |
Required current density (mA/m2)† |
---|---|---|
Bare steel |
Neutral pH, no SRB |
4.3 – 16.1 |
Neutral pH, aerated |
21.5 – 32.3 |
|
Wet, moderate to severe condition |
26.9 – 64.6 |
|
Highly acidic |
53.8 – 161.4 |
|
Supporting SRB* |
451.9 |
|
Well-coated steel |
Most of the soils |
0.01 |
†If galvanic effects are present, higher values are requires. |
||
*Sulfate-Reducing Bacteria |
Source:L.L. Sheir, R.A. Jarman, and G.T. Burstein; “Corrosion”, Volume 2: “Corrosion Control”, 3rd edition, Butterworth Heinemann, ISBN 0-7506-1077-8.
The required current density is a function of the efficiency of the coating that is applied. Table 3 shows the required current densities to protect 10 miles of 36-inch diameter pipeline with coatings of varying quality. (Note: The required current is measured according to 0.3 V voltage drop criterion). The results show that a current of 500 A is required to protect a bare structure, whereas this current can be reduced to approximately 0.5 A (the same as a two-cell flashlight bulb) when the pipeline is coated with a fairly strong coating.
Table 3.Required current densities to protect the same coating under various conditions.
Condition |
Required current density (mA/ft2) |
---|---|
Bare steel |
> 10 |
Weak coating (poor handling and installation and high degradation) |
0.012 – 0.030 |
Strong coating (good handling and installation and little or no degradation) |
3 x 10-4– 6 x 10-4 |
Perfect coating (holiday-free coating with 3/32” thickness) |
1 x 10-7 |
Source:"Peabody's Control of Pipeline Corrosion," 2nd Edition
When the required current density is rather high, designing a cathodic protection system based onsacrificial anodesis usually not recommended or even practical. It generally requires many large anodes.
Furthermore, cathodic protection with a high current is expensive because it requires high capacity rectifiers, non-consumable anodes, higher grades of connections and more power.
回到图1中,我们看到,我们可以减少the cost of cathodic protection by reducing expenses. For that reason, cathodic protection is usually applied on coated structures. Buried pipelines, ships and the undersides of liquid storage tanks are usually coated. (SeeAn Intro to Pipeline Corrosion and Coatingsfor more information.) Only rarely is it preferable to omit protective coatings, such as on offshore oil production platforms in the North Sea. In these cases, since the required current to protect cathodically is very low, sacrificial anodes are used and their design is based on a continuous current. When a coating is used the required current cannot be constant, because the coating deteriorates and leads to increasing the current density.
No coating is flawless, socathodic protection is an effective complementary methodto protect the points where a defective coating exposes structures to a corrosive environment.
Tags
Written byMehdi Yari| Electrochemistry and Corrosion Laboratory at the University of Western Ontario
![Profile Picture of Mehdi Yari](http://m.crimeawalks.com/images/uploads/human-people-person-mustache-face-portrait.jpg?width=400&height=400&mode=crop&format=jpg&quality=70&scale=both)
Mehdi Yari currently serves as a postdoctoral fellow in the Electrochemistry and Corrosion Laboratory at the University of Western Ontario. He was faculty staff in the Materials Engineering department at the Science and Research branch of Azad University (Iran) for more than eight years. During that time, he became involved in metallurgical industries as a scientific and engineering consulter. He received B.Sc., M.Sc., and Ph.D. degrees in metallurgical engineering, corrosion engineering, and advanced materials in materials engineering, respectively. He has obtained several teaching and research awards. He is author and co- author of more than 15 scientific papers in reputed journals in the field of corrosion and surface engineering.
More Q&As from our experts
Related Terms
- Corrosion Coating
- Cathodic Protection
- Pipeline Corrosion
- Anode
- Protective Coating
- Coverage
- Current Density
- Sacrificial Anode
- Disbonding
- Cathode
Related Articles
![Photo for VIDEO: Cathodic Protection in 2 Minutes Flat](http://m.crimeawalks.com/images/uploads//word-soil-lighting-furniture-tabletop-text.jpg?w=360&h=200&mode=crop&quality=70&scale=both)
VIDEO: Cathodic Protection in 2 Minutes Flat
![Photo for Cathodic Protection of Earthed Tank Farms](http://m.crimeawalks.com/images/uploads//playground-architecture-building-column-pillar-slide-toy-train-transpo.jpg?w=360&h=200&mode=crop&quality=70&scale=both)
Cathodic Protection of Earthed Tank Farms
![照片为阴极保护设计差异or FBE-Coated Pipelines](http://m.crimeawalks.com/images/uploads//dessert-donut-food-pastry-cake-meat-loaf-biscuit-brownie-chocolate-coo.jpg?w=360&h=200&mode=crop&quality=70&scale=both)
Cathodic Protection Design Differences for FBE-Coated Pipelines
Don't miss the latest corrosion content from Corrosionpedia!
Subscribe to our newsletter to get expert advice and top insights on corrosion science, mitigation and prevention. We create world-leading educational content about corrosion and how to preserve the integrity of the world’s infrastructure and assets.
- Tank Bottom Corrosion on the Soil Facing Side - Solved
- Understand and Harness Corrosion-related Regs and Acts on Infrastructure
- Over-Voltage Protection
- Using Flange Isolation Kits and Monolithic Isolation Joints
- How to Properly Spec a Monolithic Isolation Joint
- Improving Pipeline Emissions: The Role of Flange Isolation Kits
- Epoxy Coatings 101: What Kind to Use and When